Laser Preheating for Hot Crack Reduction in Direct Metal Deposition of Inconel 738LC

Soffel, Fabian ; Papis, Konrad J.M. ; et al.

In: Metals, 12 (4, 2022

Online academicJournal

Zugriff:

Volltext

Welding of precipitation-hardenable nickel-based super alloys that contain large amounts of Al and Ti is challenging due to their high susceptibility to hot cracking. For metal additive manufacturing (AM) by powder bed fusion (PBF) or direct metal deposition (DMD), various welding process adjustments may prevent the formation of cracks. The aim of this study is the development and experimental characterization of a laser preheating process for DMD of Inconel 738LC. Metallographic cross-sections of multiple test specimens were analyzed to quantify the effect of initial substrate temperature, specimen geometry, deposition parameters, and scanning strategy on the resulting crack density. The results show that increased substrate temperature by laser preheating and reduced specimen size leads to crack-free deposited structures. Therefore, the proposed preheating process may be applied for part fabrication or repair by DMD to reduce or even completely prevent the risk of hot cracking. ; ISSN:2075-4701

Titel:	Laser Preheating for Hot Crack Reduction in Direct Metal Deposition of Inconel 738LC
Autor/in / Beteiligte Person:	Soffel, Fabian ; Papis, Konrad J.M. ; 000-0002-5021-1434, id_orcid:0 ; Bambach, Markus ; 000-0002-8790-0807, id_orcid:0 ; Wegener, Konrad
Link:	http://hdl.handle.net/20.500.11850/540799 https://doi.org/20.500.11850/540799 https://doi.org/10.3929/ethz-b-000540799 https://doi.org/10.3390/met12040614 Volltext
Zeitschrift:	Metals, 12 (4, 2022
Veröffentlichung:	MDPI, 2022
Medientyp:	academicJournal
DOI:	10.3929/ethz-b-000540799
Schlagwort:	Additive manufacturing Direct metal deposition Preheating Isothermal welding Super alloy Inconel Hot cracking
Sonstiges:	Nachgewiesen in: BASE Sprachen: English Collection: ETH Zürich Research Collection Document Type: article in journal/newspaper File Description: application/application/pdf Language: English Rights: info:eu-repo/semantics/openAccess ; http://creativecommons.org/licenses/by/4.0/ ; Creative Commons Attribution 4.0 International

Klicken Sie ein Format an und speichern Sie dann die Daten oder geben Sie eine Empfänger-Adresse ein und lassen Sie sich per Email zusenden.

BibTeX Citavi, JabRef, u.a.
(Literaturverwaltung)

PDF kein Volltext!
(Merkzettel, Notizen)

RIS Endnote, Citavi u.a.
(Literaturverwaltung)

MODS
(XML zur Weiterverarbeitung)

oder

Wählen Sie das für Sie passende Zitationsformat und kopieren Sie es dann in die Zwischenablage, lassen es sich per Mail zusenden oder speichern es als PDF-Datei.

Gewünschter Zitations-Stil:

oder

Bitte prüfen Sie, ob die Zitation formal korrekt ist, bevor Sie sie in einer Arbeit verwenden. Benutzen Sie gegebenenfalls den "Exportieren"-Dialog, wenn Sie ein Literaturverwaltungsprogramm verwenden und die Zitat-Angaben selbst formatieren wollen.